低吸湿性,良好的撕裂强度,无粘性,抗撞击性,良好,低摩擦系数,可热封,耐化学性良好,耐气候影响性能良好,良好的电气性能 热成型,层压法,真空成型 | 清晰/透明 |
层压板,粘合剂 | |
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | |
密度 | ASTMD1505 | 2.15 | g/cm3 | |
DimensionalStability | AcrossFlow,Shrinkage,150°C | ASTMD1042 | 2.2 | % |
DimensionalStability | Flow,Expansion,150°C | ASTMD1042 | 0.72 | % |
DimensionalStability | 吸水率(24hr) | ASTMD1042 | <0.010 | % |
摩擦系数(与钢-动态) | ASTMD1894 | 0.10到0.30 | ||
薄膜厚度-经测试 | 25 | um | ||
抗张强度-MD | 屈服,25um | ASTMD882 | 12.0 | MPa |
抗张强度-MD | 断裂,25um | ASTMD882 | 21.0 | MPa |
伸长率-MD(断裂,25um) | ASTMD882 | 300 | % | |
弯曲模量-MD(25um) | ASTMD882 | 480 | MPa | |
埃尔曼多夫抗撕强度-MD(25um) | ASTMD1922 | 130 | g | |
GravesTear(25.0um) | ASTMD1004 | 3 | N | |
薄膜厚度-经测试 | 25 | um | ||
抗张强度-MD | 屈服,25um | ASTMD882 | 12.0 | MPa |
抗张强度-MD | 断裂,25um | ASTMD882 | 21.0 | MPa |
伸长率-MD(断裂,25um) | ASTMD882 | 300 | % | |
弯曲模量-MD(25um) | ASTMD882 | 480 | MPa | |
埃尔曼多夫抗撕强度-MD(25um) | ASTMD1922 | 130 | g | |
GravesTear(25.0um) | ASTMD1004 | 3 | N | |
ImpactStrength(25.0um) | 内部方法 | 77.0 | J/cm | |
载荷下热变形温度 | 0.45MPa,未退火,0.0250mm | ASTMD648 | 70.0 | °C |
载荷下热变形温度 | 1.8MPa,未退火,0.0250mm | ASTMD648 | 51.0 | °C |
熔融峰值温度 | ASTMD3418 | 260到280 | °C | |
比热(25°C) | 1170 | J/kg/°C | ||
导热系数(25°C) | 内部方法 | 0.20 | W/m/K | |
表面电阻率2 | ASTMD257 | >1.0E+16 | ohms | |
体积电阻率2 | ASTMD257 | >1.0E+18 | ohmscm | |
介电强度3,4 | 23°C,0.0250mm,Air | ASTMD149 | 260 | kV/mm |
介电强度3,4 | 23°C,5.00mm,Air | ASTMD149 | 70 | kV/mm |
介电常数 | 1kHz5 | ASTMD150 | 1.93到2.02 | |
介电常数 | 25°C6 | ASTMD150 | 2.00 | |
耗散因数 | 1kHz5 | ASTMD150 | 2.0E-4 | |
耗散因数 | 1MHz2 | ASTMD150 | 5.0E-4 | |
耗散因数 | 25°C6 | ASTMD150 | 2.0E-4到7.0E-4 | |
耐电弧性7(0.0250mm) | ASTMD495 | >165 | sec | |
InsulationResistance8 | 100°C | 内部方法 | 3.5E+11 | ohms |
InsulationResistance8 | 150°C | 内部方法 | 2.5E+11 | ohms |
InsulationResistance8 | 200°C | 内部方法 | 6.5E+10 | ohms |
UL阻燃等级(0.025mm) | UL94 | VTM-0 | ||
极限氧指数(0.0250mm) | ASTMD2863 | 95 | % | |
折射率 | ASTMD542 | 1.341到1.347 | ||
透射率(25.0um) | ASTME424 | 96.0 | % | |
BurstStrength-Mullen(25.0um) | ASTMD774 | 0.0760 | MPa | |
MITFoldingEndurance-film(25.0um) | ASTMD2176 | 1.0E+4 | Cycles | |
Permeability | Gas:CarbonDioxide | ASTMD1434 | 25900 | cm3/m2/atm/24hr |
Permeability | Gas:Hydrogen | ASTMD1434 | 34100 | cm3/m2/atm/24hr |
Permeability | Gas:Nitrogen | ASTMD1434 | 5000 | cm3/m2/atm/24hr |
Permeability | Gas:Oxygen | ASTMD1434 | 11600 | cm3/m2/atm/24hr |
Permeability | Vapor:AceticAcid | ASTME96 | 6.3 | g/m2/24hr |
Permeability | Vapor:Acetone | ASTME96 | 15 | g/m2/24hr |
Permeability | Vapor:Benzene | ASTME96 | 9.9 | g/m2/24hr |
Permeability | Vapor:CarbonTetrachloride | ASTME96 | 4.8 | g/m2/24hr |
Permeability | Vapor:EthylAlcohol | ASTME96 | 11 | g/m2/24hr |
Permeability | Vapor:Hexane | ASTME96 | 8.7 | g/m2/24hr |
Permeability | Vapor:Water | ASTME96 | 7.0 | g/m2/24hr |
FEP FEP Film塑料供应商,长期销售美国科慕化学生产的FEP原料,以上是“FEP Teflon® FEP Film”塑胶料的物性表参数.近期代理商可转仓交易:美国Sylvin PVC 8200-85 Black 一般目的 一般目的
法国AD MAJORIS PA6 VENYL SG108 - 8689
台湾台化 PP均聚 Formolene® 5102KR
三星第一毛织 ABS HF-0660IW 其它
德国胶宝 SEBS K TC7COZ 耐气候性能良好 汽车内部零件
兰州石化 PP C30S 纤维 流延法生产的拉丝级纤维,用于打包绳,刷子和扫帚
沈阳化工 PVC PSL-10 其它
韩国工程塑料 POM共聚 Kepital® FR-20H 耐燃油性
西班牙Triesa PBT THG4U/11 玻璃纤维增强材料20%填料按重量,刚性良好,抗紫外线性能良好
巴西Karina PVC Karina IVORY PVC COMPOUND 70900-35/1-F-IS 电子绝缘,电线电缆应用
俄罗斯西布尔 PP均聚 TOLEN H120 GP 流动性高,窄分子量分布,通用,均聚物,良好的稳定性,注射成型 通用
Generic AS(SAN) Generic SAN
中国江苏梅兰化工 氟橡胶 Jiangsu Meilan XXMLF3-14
美国陶氏 PC PC 4610-10 其它
沙伯基础 PC LEXAN™ 164R resin
● FEP 大金美国 NC-1500 其它
● FEP 沙伯基础 LNP THERMOCOMP 2X00858 compound
填料:专有填料。
● FEP 大金美国 NP-40
模塑,挤出
● FEP 美国RTP 3505
注塑
● FEP 大金美国 NP-130 其它